Investigation of various isotherm equations for mercury removal from aqueous solutions by walnut shell activated carbons
سال انتشار: 1395
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 804
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
CHCONF02_363
تاریخ نمایه سازی: 9 مرداد 1395
چکیده مقاله:
In the present investigation, the experimental data acheivied from our previous published paper were analyzed and modeled by, Sips, Toth, Unilan, Jovanovich and modified langmuir isotherms. To the best of our knowledge, Langmuir isotherm was modified and compared with various isotherm theories. Activated carbon was also prepared from walnut shell by phsical method using water vapor as the activation agent for comparison with our other carbonaceous adsorbents. The adsorption was studied by three types of activated carbon derived from walnut shell (carbon A: 1:0.5 ZnCl2 wt/wt, carbon B: 1:1 ZnCl2 wt/wt and Carbon C: Physical method). It was shown that Hg (II) adsorption follows the modified form better than the Langmuir isotherm. Langmuir assumed that each site accommodates one and only one adsorbed entity. However, it is not a precise assumption and instead the mean number of entities should be defined. The obtained equilibrium data for carbon A, B and C were modeled with Langmuir and Modified Langmuir isotherm equations. The monolayer sorption capacity of this optimum adsorbent was obtained by Langmuir isotherm as 151.5, 100.9 and 87.97 mg/g for carbon A, B and C, respectively. However, these results were determined as 174.97, 104.02 and 88.65 mg/g by modified Langmuir for carbon A, B and C, respectively.
کلیدواژه ها:
نویسندگان
Mohammad Zabihi
Department of Chemical Engineering, Sahand University of Technology, Tabriz, Iran
Khodadad Kamaliseresht
Faculty of Engineering, Petroleum University of Technology, Ahwaz – Iran
Ali Haghighi Asl
School of Chemical, Gas and Petroleum Engineering, Semnan University, Semnan, Iran
Ali Ahmadpour
Department of Chemical Engineering, Faculty of Engineering, Ferdowsi University of Mashhad, Mashhad, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :