Improving the hardness and wear resistance of magnesium alloys by TIG composite surfacing with Al+Al2O3
محل انتشار: دومین کنفرانس بین المللی کامپوزیت
سال انتشار: 1389
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,842
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
COMPOSIT02_041
تاریخ نمایه سازی: 24 مهر 1389
چکیده مقاله:
In the present study, an attempt has been made to improve the surface properties of magnesium alloys,AZ91D and AZ31, through formation of the surface composite layers with Al+Al2O3 (3:1) powder by using a Tungsten Inert Gas (TIG) process as a heat-generation source. Microstructures of composited layers were studied by optical microscope (OM) and scanning electron microscope (SEM), and phases were indicated by X-ray diffraction (XRD). The microhardness of the surface composite layers was measured and their wear behavior was also evaluated. Due to the presence of the intermetallic phase Mg17Al12 and almost uniform distribution of the ultra-hard Al2O3 ceramic particles in the grain refined Mg-rich matrix, the hardness and wear resistance of the composite coatingswere considerably improved as compared to the as-received specimens. The surface hardness increased from 80 HV0.1 and 55 HV0.1 for AZ91D and AZ31 magnesium alloys to as high as 214 HV0.1 and 230 HV0.1 for coated samples, respectively. The wear rates of composited layers were also reduced to almost 30% for both alloys
کلیدواژه ها:
نویسندگان
M. R. Elahi
MSc student
M Heydarzadeh Sohi
Professor
J Rassizadehghani
Associate Professor, School of Metallurgy and Materials
A.GH Safaei
MSc student
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :