Investigation of machinability of AISI 1045 Steel under Rolled, annealed, normalized and quench-tempered conditions
محل انتشار: همایش ملی مهندسی مکانیک
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,124
فایل این مقاله در 5 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
EASTTEHRANMECH02_083
تاریخ نمایه سازی: 9 تیر 1392
چکیده مقاله:
In this paper, machinability of AISI 1045 steels was studied in rolled, annealed, normalized, and quenchtemperedconditions. Machinability in turning was investigated based on cutting force and surface roughness. The microstructure of as received and Heat treated samples has been investigated by optical microscopy. Hardness and tensile tests was carried out on samples. Turning tests were performed at a depth of cut of 0.5mm, a feed rate of 0.05mm/rev, and cutting speeds of 13.89, 19.73, 27.79, 39.46 and 55.58m/min and dry conditions. Results show that the values of cutting force and surface roughness were in range 100 to 220N and 1 to 5μm, respectively. Quench-tempered sample shows the highest cutting force, while it shows the lowest surface roughness. As received sample has the lowest cutting force. By annealing and normalizing heat treatments, cutting force does no different significantly, but surface roughness increase.
کلیدواژه ها:
نویسندگان
H Sazegaran
Department of Metallurgy, Faculty of Engineering, University of Ferdowsi of Mashhad, Iran
A Zabbet
Department of Metallurgy, Faculty of Engineering, University of Ferdowsi of Mashhad, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :