Studying the effects of masonry Mel powder (limestone powder with a high percentage of calcium carbonate) on the mechanical properties of high strength lightweight structural concrete using expanded light particle perlite
محل انتشار: چهارمین کنفرانس بین المللی مقاوم سازی
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,437
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICCT04_407
تاریخ نمایه سازی: 7 مرداد 1392
چکیده مقاله:
Due to increased pollution problems of cement factories and its adverse impact on the environment and the high global price of this strategic material that increases the final cost of concrete, there are always a lot of efforts to achieve high strength lightweight structural concrete using indigenous and inexpensive materials that are replaced by part of the environmentally friendly cement in order to achieve sustainable development. Therefore, 204 cylindrical concrete samples were considered in 30*15 sizes with 34 mix designs, including concretes containing Mel powder (limestone powder with a high percentage of calcium carbonate) with different mix percentages. Results of this study that are obtained by implementing tests on samples made on 7 days, 28 days and 90 days demonstrated that using masonry Mel powder as 17 percent of cement weight, decrease weight of concrete and increase compressive and tensile strength of concrete using micro silica by 50 percent and increase by 30 percent in the absence of micro silica
نویسندگان
Yousef Zandi
Member of Academic Staff, Department of Civil Engineering, Tabriz Branch, Islamic Azad
Metin Husem
Department of Civil Engineering , Karadeniz Teknik University , Turkey
Arash Sohrabi
MA Student in Civil Engineering – Structure
Samad Dehghan
MA Student in Civil Engineering – Structure
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :