The effect of Ce and P loading on catalytic performance of HZSM-5 in thermal catalytic cracking of naphtha to light olefins
محل انتشار: هفتمین کنگره ملی مهندسی شیمی
سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 570
فایل این مقاله در 12 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICHEC07_365
تاریخ نمایه سازی: 25 فروردین 1394
چکیده مقاله:
In order to increase catalyst st bility and light olefins yield in catalytic cracking of naphtha, a series of HZSM-5 catalysts with various Phosphorous (0.2, 1.1 and 2 wt. %) and Cerium (2, 6 and10 wt. %) Loadings were prepared by co-impregnation method. The effect of Cerium and Phosphorous on the structure and acidity of HZSM-5 were examined by XRD, N2 adsorption/desorption and NH3-TPD. Also to study the amount of deposited coke the TGA analysis was done. The characterization results demonstrated that the structure of catalysts rarely changed by modification while the amount of acid sites increased. The results of cracking tests showed that the yield of propylene was significantly higher for Ce/P modified catalysts compared to parent catalyst while the ethylene yield did not change. Also increasing P loading the catalyst stability increased while increasing Ce loading resulted in higher propylene yield. At 680oC, the maximum Yield of ethylene and propylene were obtained about 16% and 36% respectively, for6%Ce-1.1%P/HZSM-5, while these yields showed no lost through 20 hours of reaction tests.These results revealed that there might be an optimum for acid density to maximize the Light olefins yield. In addition The TGA analysis indicates that the coke deposition is not a major factor for catalysts deactivation. So, catalyst deactivation might be attributed to the structural change.
کلیدواژه ها:
نویسندگان
Fatemeh Khodadadian
Olefin Laboratory, Faculty of Chemical Engineering Tarbiat Modares University
Jafar Towfighi
Olefin Laboratory, Faculty of Chemical Engineering Tarbiat Modares University
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :