Reheological Properties of crosslinked Poly Acrylate in Semi-batch Precipitation Polymerization
محل انتشار: هفتمین کنگره ملی مهندسی شیمی
سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 643
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICHEC07_564
تاریخ نمایه سازی: 25 فروردین 1394
چکیده مقاله:
In the present work, highly cross-linked, PAA particles were prepared under various process (batch and semi-batch process). Types of process affects very strongly on network strength. Therheological method was used to determine the strength of swollen gel. Measuring storage modulus(G') and loss modulus (G') were carried out at constant frequency and in a range of strains (0.001- 200 Pa). Furthermore, G' and G were obtained at constant strain over a range of frequencies (0.1- 100 Hz). Improving strength of network observed when sample prepared via the batch process.Finaly, the rotational viscosity was used to determine thickening properties and the pseudoplasticbehavior of samples. The semi-batch process has a good effective on increasing viscosity as compared batch process.
کلیدواژه ها:
نویسندگان
h Eshaghi
Department of Chemistry, Karaj Branch, Islamic Azad University, Karaj, Iran
h Bouhendi
Iran Polymer and Petrochemical Institute (IPPI), P.O. Box ۱۴۹۶۵-۱۱۵, Tehran, Iran
g Bagherimarandi
Department of Chemistry, Karaj Branch, Islamic Azad University, Karaj, Iran
m.j Zohurianmehr
Iran Polymer and Petrochemical Institute (IPPI), P.O. Box ۱۴۹۶۵-۱۱۵, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :