Effect of age hardening parameteres on mechanical properties of aluminium alloys series A2024 and A6061
محل انتشار: دومین کنفرانس بین المللی آلومینیوم
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,194
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IIAC02_036
تاریخ نمایه سازی: 12 اردیبهشت 1392
چکیده مقاله:
In the present work, the influence of different artificial aging conditions on mechanical properties of two types of aluminium alloys A2024 & A6061 was studied. The mechanical properties of these alloys are adjusted by performing age hardening heat treatments. For this purpose after solutionizing treatment for A2024 & A6061 at 495◦C and 529◦C and water quench. the specimens were aged at 190◦C and 170◦C respectively For different periods of time (1-10h). For The precipitation stages during ageing were monitored by hardness measurements. After different solution treatment and aging condition For each specimen, Charpy impact, hardness and tensile tests were carried out. Result reveal that During ageing the impact toughness of the alloys first increased, and then, following a maxima decreased due to the precipitation of intermediate phases, finally it reached its minimum at the peak hardness. Finally the Relationship between hardness, impact toughness and strength were investigated.
کلیدواژه ها:
نویسندگان
A.H. Moghanian
Materials Science and Engineering Department, Sharif University of Technology, Tehran, Iran
S. Feizi talarpoushti
Materials Science and Engineering Department, Sharif University of Technology, Tehran, Iran
A. Bahrami
Materials Science and Engineering Department, Sharif University of Technology, Tehran, Iran
M. Marefvand
Islamic Azad University, Karaj Branch
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :