Effect of Cooling Rate and Grain Refinement on the Microsegregation in Al-4.8 wt.% Cu Alloy
سال انتشار: 1393
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 714
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IIAC03_062
تاریخ نمایه سازی: 9 فروردین 1395
چکیده مقاله:
Microsegregation is one of the most important phenomena occurs during solidification. It usually results in formation of some unexpected second phases which generally reduce the mechanical properties and workability of casting products. The aim of this research is to study the effect of cooling rate and grain refinement on the microsegregation in Al-4.8 wt.% Cu. For this purpose two series of experiments were designed to investigate the effect of cooling rate and grain refinement on the microsegregation. In first set of experiments, the alloy was melted and cooled in three different rates, i.e. 0.04, 0.42, and 1.08 K/s in a DTA furnace. In the second series of experiments, the effect of grain refinement on the microsegregation at a constant cooling rate of 0.19 K/s was investigated. Al-5Ti-1B master alloy was used as grain refiner. Results showed that by increasing the cooling rate the amount of non-equilibrium eutectic phase increases from 5.1 to 7.4 wt.%, and the minimum concentration of solute element in primary phase is decreased from 1.51 to 1.05 wt.% Cu. But by grain refinement in alloy, the amount of non-equilibrium eutectic phase decreases from 5.5 to 4.7 wt.%, and the minimum concentration of solute element in the primary phase is increased from 0.98 to 1.07 wt.% Cu. So it is concluded that increasing cooling rate in the studied range will increase the microsegregation while grain refinement reduce the microsegregation
کلیدواژه ها:
نویسندگان
m dehnavi
Department of Materials Engineering and Metallurgy, Ferdowsi University of Mashhad, Mashhad, P.O. Box: 91775-1111, Iran
m haddad -sabzevar
Department of Materials Engineering and Metallurgy, Ferdowsi University of Mashhad, Mashhad, P.O. Box: 91775-1111, Iran
h Vafaeenezhad
School of Metallurgy and Materials Engineering, Iran University of Science and Technology (IUST), Tehran, Iran
M.H Avazkonandeh-Gharavol
Department of Materials Engineering and Metallurgy, Ferdowsi University of Mashhad, Mashhad, P.O. Box: 91775-1111, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :