EFFECT OF TiO2 ON BONDING STRENGTH OF BIOACTIVE GLASS CERAMIC COATING ON TITANIUM SUBSTRATE
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,280
فایل این مقاله در 11 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES06_137
تاریخ نمایه سازی: 8 بهمن 1391
چکیده مقاله:
The purpose of this research is to study the effect of addition of titanium dioxide on bonding strength of coating in the CaO-P2O5-Na2O-TiO2 system on titanium substrate. To achieve this, different amount ofTiO2 (2, 3.5 and 5%mol) was added to initiate batch of the glass. After production of glass powder andslurry, titanium substrate was coated with dip coating method and then heat treated to cure the coat. Finally, samples were tested with shear stress test to determine the bonding strength of the coatings and debonded surface of coating were studied by scanning electron microscopy (SEM) and compare theirproperties. The cross section of the coatings was studied using (SEM) and elemental concentration analysis by EDS along the indicated. The findings show that the coating that includes 5%mol TiO2 has the best bonding strength in comparison with the other coatings. The bioactivity of the coated samples was studied by soaking them in simulated body fluid (SBF) in order to observe the growth of an apatite layer on their surface.
کلیدواژه ها:
نویسندگان
Shima Honarvar
Master of science, Iran university of science and technology,
Bijan Eftekhari Yekta
Associate Professors, Iran university of science and technology
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :