Effect of the rotation speed on distribution of primary Si and mechanical properties of the ring (A390 alloy) by centrifugal casting
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,303
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES06_490
تاریخ نمایه سازی: 8 بهمن 1391
چکیده مقاله:
Necessity and achievement to high wear resistance and toughness components which have gradient properties in industry is improved. In this work, centrifugal casting with gradient controlling approach on A390 alloy (piston) has been studied. Casting rings at various rotation speeds 400,700 and 1000 rpm with thickness of 2cm were obtained. Microstructure characteristics and distribution of the Primary Si were assessed by optical microscopy (OM) and image analyzer software. Significant enrichment zones of primary Si particles were observed in the external and internal zone of the casting inthe radial direction of the centrifugal caster, but; in the middle layer, a few reinforcement particles were observed. Furthermore; it is found that, with increasing of the rotation speed, the thickness and volume fraction of particles in the outer layer increase. Corresponding increases in surface micro hardness as well as smaller wear volume loss in pin-on-disk wear tests in the outer layer in comparison with other layer were observed. The process provides a viable approach for high wear resistance aluminum alloy components, particularly in piston part
کلیدواژه ها:
نویسندگان
M. Mohammadi rahvard
Associate professor of School of Material Science and Engineering, Iran university of Science and Technology, Narmak, Tehran
E Rezaee kheibaree
M.S student of School of Material Science and Engineering, Iran university of Science and Technology
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :