Physical Properties of Silver Doped ZnSe Thin Films for Photovoltaic Applications
سال انتشار: 1392
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 586
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJEE-5-1_013
تاریخ نمایه سازی: 1 اردیبهشت 1393
چکیده مقاله:
Closed space sublimation (CSS) technique was used to deposit pure (99.99%) zinc selenide(ZnSe) powder on to glass substrates for fabricating the ZnSe thin films. The temperatures of source, substrate andthe deposition time were optimized to deposit thin films of different thicknesses. Silver (Ag) was used as adopant by ion exchange process in the ZnSe thin films. The structural analysis showed that as-deposited ZnSe thin films were polycrystalline having preferred orientation [111] direction. Micro structural parameters such as crystallite size, lattice parameter were determined using X-rays diffraction (XRD). Grains boundaries,roughness on surface and the grain density of the thin film samples were measured by scanning electron andatomic force microscopy before and after Ag doping.As-deposited, Ag-doped ZnSe samples before and after annealing were optically characterized by spectrophotometer in ultra violet, visible and infrared regions. The energy band gap of as-deposited ZnSe thin films for varying thicknesses were ranging from 2.62-2.67 eV whichwas reduced after Ag doping.The electrical properties showed that as-deposited thin films were highly resistive of the order of 108 -cm and after Ag immersion, it was reduced to 1 -cm. Deposition parameters and Ag doping influenced the structural, surface, optical and electrical properties
کلیدواژه ها:
ZnSe thin films Vacuum coating Surface morphology Electrical properties
نویسندگان
Nazar Abbas Shah
Thin Films Technology (TFT) Research Laboratory, Department of Physics,COMSATS Institute of Information Technology, Islamabad ۴۰۰۰۰ Pakistan
Mussart Abbas
International Islamic University, Islamabad ۴۰۰۰۰ Pakistan
Waqar Adil Syed
International Islamic University, Islamabad ۴۰۰۰۰ Pakistan
Waqar Mahmood
Thin Films Technology (TFT) Research Laboratory, Department of Physics,COMSATS Institute of Information Technology, Islamabad ۴۰۰۰۰ Pakistan