Curing Kinetics Modification of Resole Type Phenolic Resin used inPreparation of Solid Fuel Projectile’s Nozzle

سال انتشار: 1396
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 564

فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:

شناسه ملی سند علمی:

MECHAERO02_322

تاریخ نمایه سازی: 13 شهریور 1396

چکیده مقاله:

In the present work, novel curing solution was used to cure resole type phenolic resin which widely used in solid fuel projectile’s nozzle. Effect of para-toluene sulfonic acid as accelerator and sodium bicarbonate and urea as a retardant on curing kinetics was investigated. Curing rate of resole resin increased by increasing temperature and para-toluene sulfonic acid concentration. Curing rate of resole decreased by increasing sodium bicarbonate amount in curing solution. Curing behavior of resole resin was amazing in the presence of urea in curing solution. There was two stage at curing of resole with this novel curing solution. At the first stage resole cured partly but it flows well and at second stage resole cured completely. Sheets of chopped fiber glass impregnated with modified curing solution was prepared. Three-pointbending test of these sheets shows that strength at break increased 78% and the oxyacetylene flame test showed improved thermal resistance

کلیدواژه ها:

نویسندگان

Hojat Rajabzadeh

Metallurgy Department, Malek-Ashtar University of technology, Tehran, Iran,

Mohammad rezaei

Composite Department, Iran Polymer and Petrochemical Institute (IPPI), Tehran, Iran,

Tahmoures Keshavarz

Novel Drug Delivery Systems Department, Iran Polymer and Petrochemical Institute (IPPI), Tehran, Iran,