Investigation Of Dissolution Ag and Cu In Cu-Ag Nanocomposite By Using Mo interface
محل انتشار: همایش ملی مهندسی شیمی
سال انتشار: 1388
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,741
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
NCCEESLAMSHAR01_078
تاریخ نمایه سازی: 9 آبان 1388
چکیده مقاله:
In this investigation, Initially, Copper and Silver powders were milled at 30h. In the next step,primarily milled Copper and Molybdenum powders and then milled Silver powder were compressed under 250 Mpa, by using metallic die. These compacts samples were heated at 1 hour at 473 K and 673 K. Samples were studied by SEM and XRD. The results prove that the forming of supersaturated solid solution and decomposing to Cu-Ag nanocomposite. SEM images show that there is little diffusion at 473 K while has been increased at 673 K.
کلیدواژه ها:
نویسندگان
S.M.M Shafiei
Student of Msc- Nanomaterials Engineering, Materials and Energy Research Center (MERC),Iran
E Salahi
Assistant Prof.- Materials and Energy Research Center (MERC),Iran
S.A Tayebi fard
Assistant Prof.- Materials and Energy Research Center (MERC),Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :