Evaluation of failure mechanism on Zirconia Reinforced alumina composites using by unsupervised clustering technique

سال انتشار: 1392
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 804

فایل این مقاله در 13 صفحه با فرمت PDF قابل دریافت می باشد

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:

شناسه ملی سند علمی:

NCMII01_388

تاریخ نمایه سازی: 22 اردیبهشت 1393

چکیده مقاله:

The objective of this study is to utilize Principal component analysis (PCA) and Fuzzy clustering Means (FCM) as unsupervised clustering technique for the evaluation and classification of failure mechanism based on the analysis of the acoustic emission (AE) signals of presented. Materials used were two kinds of alumina and any kinds of zirconia reinforced alumina composite (ZrO2/Al2O3) specimens with the different microstructure, subjected to a three point bending test. Different AE sources are characterized and as a result, two types of failure mechanisms are distinguished. It is observed that at very low strain levels void nucleation is the main source for AE. At higher levels, the micro pop-in of primary voids and their eventual coalescence results in a different type of AE. In fine particle reinforced materials, when the amplitude of AE events in void nucleation at fine particles is not high enough to be detected, the main source of AE events is only the void coalescence

نویسندگان

Jahan Taghizadeh

Assis. Prof., Mechanical Engineering Faculty, Qom University of Technology, Qom, Iran P. O. B. ۳۷۱۹۵-۱۵۱۹ Qom

مراجع و منابع این مقاله:

لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :
  • . Lange, F.F. Tran sformation toughening: Part 4 _ Fabrication ...
  • . Fischer H.; Marx R. Fracture toughness of dental ceramics: ...
  • . Branemark P.I.: Zarb G. A.; Albrektsson I Tis sue-integrated ...
  • . Sadoun M.; Perelmuter S Alumina- zirconia machinable abutments for ...
  • . ASM Handbook: Nondestructive Evaluation _ Quality Control, vol.17, ASM ...
  • . Hannink, R.H.J. Tran sformation toughening in Zirconia- Containing Ceramics, ...
  • -[6]. Fischer H.; Rentzsch, W.; Marx, R. Elimination of low-quality ...
  • . Keith, O.; Kusy, R.P.; Whitey J.Q. Zirconia brackets: an ...
  • . Cando, D.C. Zirconia: _ alternativa fiable, Labor Dental, v. ...
  • . Ardlin, B.I. Tran S formation -toughened zirconia for dental ...
  • . Prestipino, V. and Ingber, A. All-ceramic implant abutments: Esthetic ...
  • . Christel, P.; Meunier, A.; Heller, M; Torre, J.P.; Peille, ...
  • . Affatato, S.; Goldoni, M.; Testoni, M.; Toni, A. Mixed-oxides ...
  • . Serra, E.; Tucci, A.; Esposito, L.; Piconi, C. Volumetric ...
  • . Piconi, C.; Maccauro, G. Zirconia s a ceramic biomaterial, ...
  • . Wang, J.; Stevens, R. Review zirconia- toughened alumina(ZTA) ceramics, ...
  • . Claussen, N.J.; Fracture toughness of Al, O, with an ...
  • . Hori, S.; Yoshimura, M.; Somiya, S. S trength -toughnes ...
  • . Evans, A.G.; Perspective _ the development of high-toughness ceramics, ...
  • . Casellas, D.; Rafols, I.; Llanes, L.; Anglada, M. Fracture ...
  • . Gregori, G.; Burger, W.; Sergo, V. Piezo- spectroscopic analysis ...
  • . Karihaloo, B.L. Contributions of t-m phase transformation to the ...
  • . Becher, P.F.; Alexander, K.B.; Warmick, W. Influence of ZrO ...
  • . Fantozzi, G.; Orange, G. Thermo mechanical properties of zirconia ...
  • . ASTM: C1327-99, Standard test method for Vickers indentation hardness ...
  • . ASTM: C-1421-99, Standard test method for determinatiow of fracture ...
  • -I27]. Anstis, G.R.; Chantikul, P.; Lawn, B.R.; Marshall, D.B. A. ...
  • نمایش کامل مراجع