Kinetics of Formation and Gelation Behavior of the Poly (urethane-isocyanurate)

سال انتشار: 1382
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,748

فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:

شناسه ملی سند علمی:

NICEC08_353

تاریخ نمایه سازی: 8 اسفند 1386

چکیده مقاله:

Kinetics of formation of poly(urethane-isocyanurate) (PUIR) from toluene diisocyanate (TDI) and polypropylene glycol (PPG) in presence of dibutyltin dilaurate (DBTDL) was investigated and the kinetic parameters of simultaneous reactions of urethane and isocyanurate formations have been obtained. The gelation behavior of PUIR was studied in the conventional batch reactor as well as in the internal mixer. The results showed that the gelation time can be expressed as a power function of DBTDL concentration. The torque and temperature evolutions were used to present the extent of crosslinking reactions during the formation of PUIR in the internal mixer. The gelation is expedited with increasing r-value, catalyst concentration, temperature and mixing rate. The maximum and final values of torque and temperature, are not so much influenced by catalyst concentration in the mixer. The PUIR samples have been characterized using various measurements.

نویسندگان

Navarchian

Polymer Group,Tarbiat Modarres University,Tehran, Iran.

Semsarzadeh

Polymer Group,Tarbiat Modarres University,Tehran, Iran.

Morshedian

Iran Polymer and Petrochemical Institute, Tehran, Iran.

مراجع و منابع این مقاله:

لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :