Manufacturing of a nano composite for implying in bipolar plate of PEMFC
محل انتشار: چهارمین همایش پیل سوختی
سال انتشار: 1389
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,291
فایل این مقاله در 17 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
PEEL04_101
تاریخ نمایه سازی: 25 خرداد 1390
چکیده مقاله:
This paper investigates the effects of pressure, filler contents and type of fillers on through-plane and in-plane electrical conductivity, mechanical properties (flexural strength and hardness), density, porosity and water absorption of Phenolic resin/Graphite composite. This composite is a candidate for employing in bipolar plate. The composite was manufactured by hot compaction method. In this research two pressure 15 and 740 bars have been applied in 20, 30, 40, 50, 60, 70 and 80 %wt graphite contents as filler. The Characterization was also conducted by an optic microscope, a stereoscope (for porosity characterization) and SEM (for characterizing fracture mechanism). The results showed that the pressure considerably affect on all of properties and can dramatically change the porosity percentage of composite. The mechanical properties were maximized in about 40%wt. It was found that the single reinforcing filler constituent composite plates do not provide the requisite properties for the purpose of being used as the bipolar plate. Hence the Phenolic resin/Graphite composite plates were modified by nanosheet expanded graphite and carbon fiber (in order to improve electrical conductivity and mechanical strength respectively). These samples were fabricated in 5, 10 and 20%wt of expanded graphite and 5%wt of carbon fiber. In the optimum composition (P/40%G/5%EG/5%CF), the in-plane electrical conductivity, through-plane electrical conductivity and flexural strength of composite bipolar plates were produced with of 1518 S/cm, 76 S/cm and 84 Mpa respectively that perform DOE guideline. In this work contact resistance between bipolar plate and GDL (gas diffusion layer) was determined by changing pressure.
کلیدواژه ها:
نویسندگان
R Taherian
Department of Material Engineering of Shiraz university, Shiraz, Iran
A Nozad Golikand
Corrosion La. & Material Research Institute, NSTI, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :