Preparation and Investigation of Mechanical and Antibacterial Properties of Poly (ethylene terephthalate)/Chitosan Blend
محل انتشار: کنفرانس بین المللی فرآورش پلیمرها
سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,360
متن کامل این مقاله منتشر نشده است و فقط به صورت چکیده یا چکیده مبسوط در پایگاه موجود می باشد.
توضیح: معمولا کلیه مقالاتی که کمتر از ۵ صفحه باشند در پایگاه سیویلیکا اصل مقاله (فول تکست) محسوب نمی شوند و فقط کاربران عضو بدون کسر اعتبار می توانند فایل آنها را دریافت نمایند.
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
PPSRC2011_213
تاریخ نمایه سازی: 30 بهمن 1390
چکیده مقاله:
Chitosan, a polymer of glucosamine, is industrially produced by chemical deacetylation of chitin separated from shellfish. The aim of this work was to evaluate the anti-bacterial and mechanical properties of chitosan based solvent-cast blends with synthetic PET. For the PET/Chitosan blend, the amount of chitosan loading was varied from 1% to 9% (W/W). Chitosan and PET were homogeneously dissolved in a ternary solvent system with different mass ratios in a triflouro acetic acid, chloroform, and acetic acid solution and processed into uniform films. Molecular interactions between chitosan and PET were investigated using Attenuated Total Reflectance-Fourier Transform Infrared (ATR-FTIR) spectroscopy. Morphology and tensile properties of these blend films were investigated. The antibacterial activity of the samples was evaluated utilizing the colony forming unit method against three typical human pathogenic microorganisms, Escherichia coli, Klebsiella pneumonia, and Staphylococcus aureus. The results indicated that the PET/chitosan films showed a significantly higher growth inhibition rate compared with the PET film. Chitosan release from a wide range of blends was studied using the Ninhydrin method. The release tests revealed that dissolution of the biocide glucosamine groups, i.e. the chitosan water soluble fractions, also increased with the increase in the amount of chitosan content. Results obtained from ATR-FTIR spectra suggested that there exist pronounced interactions that probably resulted from hydrogen bond formation between different components. SEM micrographs showed that the compatibility of the two polymers was reduced when the fraction of chitosan was increased. Tensile strength and elongation at break of the blends decreased with the increase in chitosan content. With the increase in chitosan content from 1 to 9%, the tensile strength tends to decrease from 50.0 to 26.6 MPa and elongation at break decreases from 78.5% to 21.1%. These results indicated that the blends became brittle with increasing the chitosan content
کلیدواژه ها:
نویسندگان
Masoud Tavangar
Department of Chemical Engineering (Polymer group), Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :