Effect of particle size of water-base core-shell latexes of butylacrylate and methylmethacrylate on minimum film formation temperature
عنوان مقاله: Effect of particle size of water-base core-shell latexes of butylacrylate and methylmethacrylate on minimum film formation temperature
شناسه ملی مقاله: ICHEC07_003
منتشر شده در هفتمین کنگره ملی مهندسی شیمی در سال 1390
شناسه ملی مقاله: ICHEC07_003
منتشر شده در هفتمین کنگره ملی مهندسی شیمی در سال 1390
مشخصات نویسندگان مقاله:
Khadijeh Didehban - Polymer Science Department, Iran Polymer and Petrochemical Institute, P.O. Box: ۱۴۹۶۵/۱۱۵, Tehran, Iran
Iraj Hasanzadeh - Polymer Science Department, Iran Polymer and Petrochemical Institute, P.O. Box: ۱۴۹۶۵/۱۱۵, Tehran, Iran
Ali Reza Mahdavian - Polymer Science Department, Iran Polymer and Petrochemical Institute, P.O. Box: ۱۴۹۶۵/۱۱۵, Tehran, Iran
Mohammad reza Rhnama - Polymer Science Department, Iran Polymer and Petrochemical Institute, P.O. Box: ۱۴۹۶۵/۱۱۵, Tehran, Iran
خلاصه مقاله:
Khadijeh Didehban - Polymer Science Department, Iran Polymer and Petrochemical Institute, P.O. Box: ۱۴۹۶۵/۱۱۵, Tehran, Iran
Iraj Hasanzadeh - Polymer Science Department, Iran Polymer and Petrochemical Institute, P.O. Box: ۱۴۹۶۵/۱۱۵, Tehran, Iran
Ali Reza Mahdavian - Polymer Science Department, Iran Polymer and Petrochemical Institute, P.O. Box: ۱۴۹۶۵/۱۱۵, Tehran, Iran
Mohammad reza Rhnama - Polymer Science Department, Iran Polymer and Petrochemical Institute, P.O. Box: ۱۴۹۶۵/۱۱۵, Tehran, Iran
The film formation process of emulsion copolymers is obviously of great importance. In the present work, polymeric particles of butylacrylate and methylmethacrylate are prepared with coreshell morphology and the relationship between the particle size of an emulsion copolymer system and the minimum film formation temperature (MFFT), were investigated. By means of different monomer/emulsifier ratio feed in polymerization system a series of latexes with polymericparticles ranging 46-960 nm were prepared and MFFT and some final film properties were studied. Results indicate that decrease in particle size lead to decrease in MFFT and as well slightly decrease in molecular weight
کلمات کلیدی: emulsion polymerization, particle size, minimum film formation temperature, water base latex