Highly Open Porous Emulsion‒Templated Monoliths: Effect of Electrolyte and Organoclay
عنوان مقاله: Highly Open Porous Emulsion‒Templated Monoliths: Effect of Electrolyte and Organoclay
شناسه ملی مقاله: ICHEC07_550
منتشر شده در هفتمین کنگره ملی مهندسی شیمی در سال 1390
شناسه ملی مقاله: ICHEC07_550
منتشر شده در هفتمین کنگره ملی مهندسی شیمی در سال 1390
مشخصات نویسندگان مقاله:
s Sadeghi
m.r moghbeli - Corresponding Author address: School of Chemical Engineering, Iran University of Science and Technology, Tehran, Iran
خلاصه مقاله:
s Sadeghi
m.r moghbeli - Corresponding Author address: School of Chemical Engineering, Iran University of Science and Technology, Tehran, Iran
Highly open porous polymer foams were prepared by polymerization of water-in-oil high internal phase emulsions (HIPEs) that contain styrene, acrylonitrile and divinylbenzene. The effect ofelectrolyte and two different contents of organo-modified montmorillonite (Cloisite30B, C30B) on the HIPE equilibrium torque values, an approximate characterization of HIPE viscosities, and the microstructure and properties of the resulting PolyHIPE foams were investigated. The resultsshowed by adding electrolyte to the aqueoues phase of the emulsion, torque fluctuations decreasedand the stability of the emulsion increased. Scanning electron micrographs exhibited an open-cell polyHIPE structure for all of the samples. The weigth-average diameter of the cells and intercellular windows of the foam without organoclay were 26.4μm and 7.7μm, respectively. Theintroduction of organoclay within the emulsion copolymer foam significantly decreased the mean size of cells and intercellular windows compared with the copolymer foam without reinforcement. According to compression results by using 1%wt C30B in the organic phase the Young’s module and crush strength of the sample increased about 33.5% and 171%, respectively
کلمات کلیدی: emulsion polymerization, nanocomposite foams, Cloisite 30B, mechanical properties