Modification of Physical and Chemical Properties of Mastic Joint by Bentonie-impregnated in Waste Oil and Sulphur
محل انتشار: کنفرانس بین المللی پژوهش در علوم و تکنولوژی
سال انتشار: 1394
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 416
فایل این مقاله در 13 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
CRSTCONF01_633
تاریخ نمایه سازی: 27 اسفند 1394
چکیده مقاله:
Shrinkage cracks and rutting in pavement occurs in streets due to temperature changes in different seasons. Filling the cracks with elastomeric bituminous sealants is one of the convenient ways to prevent development of cracks. Low strength and flexibility, incoherence, low stability, lack of resistant against penetration and expensive ingredient are sealant's problems. Therefore, the aim of this study is the modification of sealant to cut down costs, by using waste Sulphur and oily waste bentonite from refining oil factories. The use of waste material, in addition to reducing costs, solves the environment problems. In this investigation, several amounts of Sulphur and oily Bentonite was added to basic sealant material (bitumen 60/70, SBS and talc) and then the rheological, physical and mechanical properties of the blend were studied. It is found that addition of Sulphur to basic mastic causes: 1- High strength and resistance to penetration, 2- High thermal stability, 3- Cross linking and inability to re-melt, 4- promoting G*, 5- improving rutting resistance. It is found that the 160°C temperature is not a suitable temperature for SBS modified asphalt with every percentage of sulphur and in this temperature a gel component may be formed. Addition of oily bentonite besides sulphur to mastic causes: 1- decreasing density, 2- Increasing flexibility, 3- improving G*.
کلیدواژه ها:
نویسندگان
Azade Najafghlizade
My Institute/Company Tehran, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :