Preparation of Polysulfone nano-structured membrane for removal metal ions from water
سال انتشار: 1388
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,188
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICAWTR01_036
تاریخ نمایه سازی: 20 اردیبهشت 1390
چکیده مقاله:
Polysulfone nanofiltration (NF) membranes with higher pore size and higher charge density are capable of removing metal ions from water. Therefore the present study concerns the graft-modification of ultrafiltration (UF) membranes by UV irradiation. UF membranes were prepared via phase inversion method. Polyethylene glycol (PEG) with molecular weights 1500, 3000 and 4000 gr/mol was used in casting solution as comparatively big sized pore former. Effect of grafting conditions including monomer concentration and irradiation time on membrane performance properties as pure water flux (PWF) and salt rejection were studied. FTIR-ATR, SEM and AFM were employed to characterize the chemical and structural changes on the modified membrane surface. The result showed PWF significantly declines and salt rejection improves with increase in both graft irradiation time and monomer concentration. At 25 °C, PWF of this prepared NF membrane is 13.26 m3.m-2.h-1 at 300 kPa. The rejection to different salt solutions follows the decreasing order of Na2SO4 (96.3%), MgSO4 (58.8 %), NaCl (51 %) and CaCl2 (28.6%). The RMS roughness of this membrane is 1.65 nm which is NF membrane properties range
کلیدواژه ها:
نویسندگان
A Akbari
Nano Science Technology Center, University of Kashan, Kashan, Iran
M Homayoonfal
Nano Science Technology Center, University of Kashan, Kashan, Iran