Influence of heat treatment of sycamore and spruce wood on tensile adhesion strength of transparent coatings

سال انتشار: 1394
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 431

متن کامل این مقاله منتشر نشده است و فقط به صورت چکیده یا چکیده مبسوط در پایگاه موجود می باشد.
توضیح: معمولا کلیه مقالاتی که کمتر از ۵ صفحه باشند در پایگاه سیویلیکا اصل مقاله (فول تکست) محسوب نمی شوند و فقط کاربران عضو بدون کسر اعتبار می توانند فایل آنها را دریافت نمایند.

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:

شناسه ملی سند علمی:

ICCC06_278

تاریخ نمایه سازی: 25 بهمن 1394

چکیده مقاله:

The aim of this study was to investigate the effect of heat treatment on adhesion strength of transparent coatings. Heat treatment is one of the processes used to modify the properties of wood. Heat-treated wood (thermowood) is considered an eco-friendly alte rnative to chemically impregnated wood materials. For this purpose, specimens with 150×100×20 mm3 of Sycamore and Sp ruce wood exposed to heat treatment at 160 and 180 °C for ٣ hours. After heat treatment, surfaces of all specimens sanded and coated with transparent coatings in two separate processes: sealer-clearer water-based coating and water-based special coating for Thermowood. The tensile adhesion strength (Pull-off) and scratch Cross-Cut was measured according to ASTM D-4541 and AS TM D 3359, respectfully. The results revealed that by increasing the temperature of heat treatment, adhesion strength was redu ced. The decrease in the sealer-clearer coating was statistically significant. However, there was no significant difference observed between different temperatures for Thermowood special coating. It was also found that the adhesion strength of coating in Spruce wood was higher than Sycamore wood. The highest adhesion strength was obtained in the Thermowood special coat ing in heat-treated specimens at 160 °C and the least observed in sealer-clearer coating in heat-treated specimens at 180 °C.

کلیدواژه ها:

Adhesion strength - Sycamore - Spruce - Transparent coatings- Heat treatment

نویسندگان

A. Talaei

Assistant Professor at Department of Wood Science and Technology, Faculty of Civil Engineering, University of Shahid Rajaee Teacher Training, Tehran, Iran

M. Tavakoliyan

Department of Wood Science and Technology, Faculty of Civil Engineering, University of Shahid Rajaee Teacher Training, Tehran, Iran.

مراجع و منابع این مقاله:

لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :
  • Welzbacher C.R., Rassam G., Talaei A. & Brischke C. (201 ...
  • Tjeerdsma, B. and Militz, H. 205. Chemical changes in hydrothermal ...
  • نمایش کامل مراجع