The Effect of Super Viscose and Air Entrainment on Reducing Corrosion of Light Concrete with Leca Aggregate
محل انتشار: نهمین کنگره بین الملی مهندسی عمران
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,163
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICCE09_981
تاریخ نمایه سازی: 7 مهر 1391
چکیده مقاله:
Due to high humidity in coastal areas, concrete framework structures are more common than metal framework structures. However, corrosive ions and salts such as chlorine, sodium, various sorts of sulfates and destructive particles within fog made in these areas, In addition to continuous cycles of structures that become dry and wet ,cause aggravating in destruction of buried concretes in earth and concrete which is in the direct contact with air or sea water proximity. On the other hand, since light concrete generally has more porosity and higher water absorption, it has less strength against the adverse items. That is why deploying light concrete, in spite of its numerous advantages, has not been expanded in coastal areas. In sum, this paper dealt with analysis of effects of viscose materials, air entrainment and anti-sulfate cements upon concrete corrosion, it was done by performing pressure and electric resistance experiments, and comparing the amount of water absorption in the light concrete models that were constructed with artificial leca aggregate
کلیدواژه ها:
نویسندگان
Javadreza Vahedi
Faculty Member of Bojnourd University
Afshin Poursalimi
Civil Engineering Student of Bojnourd University
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :