The Optimum range of ECAP Passes on a Mg Alloy in Terms of Homogeneity, Strength and Ductility: Experimental Study
سال انتشار: 1396
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 319
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICCEAS01_039
تاریخ نمایه سازی: 26 مرداد 1397
چکیده مقاله:
In this study, different passes of Equal Channel Angular Pressing (ECAP) was applied on Mg-Al-Mn (AM) series magnesium alloy to investigate the microstructure and mechanical properties. ECAP process was carried up to 4 passes using route BC, where the samples are rotated by 90º in the same direction between consecutive passes. Microstructures were studied using optical microscope (OM) and scanning electron microscope (SEM) and it was observed that the grain size was reduced from 100 μm to 1 μm after 4 passes. Tensile test was conducted and the ultimate tensile strength (UTS) increased up to 2 passes but decreased with higher passes, even though grain size became finer with increase in ECAP passes. Microhardness was carried out and it was observed that the hardness was increased up to 2 passes of ECAP and decreased with higher passes.
نویسندگان
Parham Rostami
M.S.c graduated, Department of Mechanical engineering, University of Tehran, Iran