Synthesis and characterization of W-type zeolite membrane:effect of synthesis temprature
محل انتشار: هفتمین کنگره ملی مهندسی شیمی
سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 583
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICHEC07_750
تاریخ نمایه سازی: 25 فروردین 1394
چکیده مقاله:
In this paper, effects of synthesis temperature on synthesis of W-type zeolite membrane were investigated. Experiments were carried out at these levels of synthesis temperature: 165, 185 and 200 °C and synthesis time: 12. Permeation measurements and SEM analysis were used forcharacterization of the synthesized membranes. The results showed that increasing synthesis temperature from 165 up to 185 °C increases separation factor of O2/SF6, however, furtherincreasing decreases the separation performance. The same trend was observed for synthesis time for the synthesized zeolite W membrane. This behavior was attributed to the effect of synthesis temperature on selectivity. More zeolite crystals are deposited, and larger crystals are formed at higher synthesis temperatures. Formation of larger crystals increases zeolite layer integration rate,which is responsible for gas separation, in one hand and reduces deposited zeolite layer density, due to the more void formation, on the other hand. In the optimum condition, W-type zeolite membrane was synthesized at 185 °C for 12 h with a high separation factor of 12.
کلیدواژه ها:
W-type zeolite membrane ، Gas separation ، Optimum synthesis condition ، effect of synthesis temptature
نویسندگان
Hojjatollah Maghsoodloorad
Research Centre for Membrane Separation processes, Faculty of Chemical Engineering, Iran University of Science and Technology, Narmak, Tehran, Iran
Toraj Mohammadi
Research Centre for Membrane Separation processes, Faculty of Chemical Engineering, Iran University of Science and Technology, Narmak, Tehran, Iran
Afshin Pak
Research Centre for Membrane Separation processes, Faculty of Chemical Engineering, Iran University of Science and Technology, Narmak, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :