The Effect of Machining on the Microstructure in Hybrid Welding/Milling based Rapid Prototyping.
سال انتشار: 1384
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,319
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICME07_078
تاریخ نمایه سازی: 6 آذر 1388
چکیده مقاله:
A hybrid RP process, based on welding and milling shows good promise to produce dense, and dimensionally accurate metallic parts and tools. In this paper a comparison of the microstructure is made between weld based prototype parts, produced both with and without machining after each deposited layer. It has been found that there exists a sequential fluctuating behavior in the microstructure and grain size in the deposit without machining (DWM). This behavior, however, is only confined in the top layer of the deposition with intermediate machining (DWIM). The results show that a part built by DWIM, as compared to DWM, will result in comparatively homogenous microstructure.
کلیدواژه ها:
نویسندگان
R.A Mufti
PhD. Student Faculty of Mechanical Engineering, Ghulam Ishaq KhanInstitute of Engineering ۱Sciences and Technology, Topi ۲۳۴۶۰, Pakistan
M.P Mughal
Associate Professor Faculty of Mechanical Engineering, Ghulam Ishaq KhanInstitute of Engineering ۱Sciences and Technology, Topi ۲۳۴۶۰, Pakistan
A.A Khan
Associate Professor
H Fawad
PhD. Student
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :