Formation of wear resistance surface alloyed layers on AZ31B substrate using TIG welding technique
سال انتشار: 1384
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,468
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICME07_128
تاریخ نمایه سازی: 6 آذر 1388
چکیده مقاله:
Tungsten inert gas (TIG) welding process has been employed to produce surface alloyed layers on preplaced magnesium substrate (AZ31B) with Al to improve wear resistance. The effect of TIG heat input on geometry, porosity and dilution of the surface alloyed layers has been investigated. Characterization of the surface alloyed layers have been carried out using optical and scanning electron microscopy, X-ray diffractometry, energy dispersive spectroscopy, microhardness and wear resistance testing. The microstructures of the surface alloyed layers showed the presence of Mg17Al12 based intermetallic compound within the α-Mg matrix. A maximum microhardness value of 170 HV was found in the surface alloyed layer, which is around three times of that of the substrate material (50 HV). Wear tests exhibited the better performance of the surface alloyed AZ31B than the untreated material.
کلیدواژه ها:
نویسندگان
T Mosarrezaie
M. Sc. Student School of Metallurgy and Materials Engineering,Faculty of Engineering, University of Tehran, Iran
S.F Kashani Bozorg
Assistant Professor
H.M Ghasemi
Associate Professor
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :