Studying behavior of Al-composite reinforced by ZrSiO4 /TiB2 under different processing temperature
سال انتشار: 1386
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,881
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICME08_133
تاریخ نمایه سازی: 27 آبان 1388
چکیده مقاله:
Recently, a large number of metal-matrix composites (MMCs) have been developed for high performance applications. The first requirement for superior performance of a composite material is the homogeneous distribution of the reinforcing phase. In particulate-reinforced composites, any agglomeration of reinforcement particles deteriorates the mechanical properties of composite. In present study, ZrSiO4 and TiB2 particles were incorporated in A356.1 alloy. The size of ZrSiO4 and TiB2 particles was 1 micron. Reinforcement particles were added to melted aluminum at different temperatures above pure aluminum melting point (750, 850, 950ºC). The volume percent of reinforcement particles was 5%. After addition of reinforcement, stirring was continued for 12 minutes for better distribution and better solidification conditions. The microstructure and mechanical behavior of prepared composites were studied. The results of these experiments show that the mechanical properties and microstructure of composites were changed by increasing temperature; also the best condition of ZrSiO4 case was 750ºC but 850ºC for TiB2.
کلیدواژه ها:
نویسندگان
K Shirvani Moghaddam
M.Sc.Azad University of South Tehran, Tehran, Iran
H. R. Baharvandi
Phd-School of Metallurgy and Materials Engineering-University of Tehran, Tehran, Iran
H Abdizadeh
Phd-Malek Ashtar University of Technology, Tehran, Iran
N Ehsani
Phd-Malek Ashtar University of Technology, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :