Hardness and tensile strength of zircon particles and TiB2 reinforced Al-A356. 1 alloy matrix composites :Comparative study
سال انتشار: 1386
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,471
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES01_187
تاریخ نمایه سازی: 29 اسفند 1390
چکیده مقاله:
Aluminum matrix composites are important engineering materials in automotive, aerospace, thermal, wear, and other applications because of excellent low weight, high specific strength, and better physical and mechanical propertiescompared to pure aluminum. In this paper, zircon and TiB2 ceramic particles with different amounts were incorporatedinto Al-A356.1 alloy by stir-casting route. The ceramic particles size and adding temperature were 1 micron and 750°Crespectively. Microstructure of samples has been investigated by scanning electron microscopy (SEM); hence thedispersion of reinforcement was noted. Situation of compounds of composites was examined by XRD. Mechanical tests such as hardness measurement, tensile and physical (density) tests were used. Results showed that the mechanicalproperties and microstructure behavior of composites have improved compared to monolithic alloy. Microstructures ofthe composites in as-cast conditions show uniform distribution particles and reveal better bonding in the case of zirconreinforced composite compare to TiB2, but increasing the amount of reinforcement shows better conditions in the case ofTiB2 reinforced composite. It is observed that TiB2 reinforced composites have a better wetting condition compare tozircon reinforced composites
کلیدواژه ها:
نویسندگان
K. Shirvani Moghaddam
eAzad University of South Tehran, Tehran, Iran
H. Abdizadeh
bSchool of Metallurgy and Materials Engineering-University of Tehran, Tehran, Iran
H. R. Baharvandi
dMalek Ashtar University of Technology, Tehran, Iran
N. Ehsani
dMalek Ashtar University of Technology, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :