OXIDATION BEHAVIOR OF KOVAR ALLOY IN AIR ATOMOSPHERE
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,854
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES06_448
تاریخ نمایه سازی: 8 بهمن 1391
چکیده مقاله:
The excellent match of thermal expansion between Borosilicate glasses and Kovar alloy eventuated to use these materials in production of seal parts similar; microelectronics devices, thermal receivers. According to nonmetallic properties of glasses, making metallurgical bound between metal and glass direct is almostimpossible because of wettability conditions. This problem can be solved by producing intermediate oxide layer, on the surface of Kovar. The oxidation of the Kovar alloy experiments at air atmosphere were conducted by using resistance tubular furnace. Changes in temperature and time factors resulted differentoxide layer thicknesses. XRD studies showed that the oxide layer mainly consists of Fe2O3 and Fe3O4. The layers' thicknesses were evaluated by scanning electron microscopy at 750°C for 10min. According to the results, to have an optimum oxidation process, with an optimum thickness, a controlled atmosphere is necessary.
کلیدواژه ها:
نویسندگان
Aboalfazl Ebrahimi
Department of Materials Engineering, Semnan University, Semnan, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :