SYNTHESIS OF NITINOL ALLOY POWDER BY ELECTROLESS PLATING
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 971
فایل این مقاله در 12 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES06_538
تاریخ نمایه سازی: 8 بهمن 1391
چکیده مقاله:
In the present research, the Nitinol powder was prepared by electroless nickel plating and heat treatment of titanium powder. Hydrazine reducing agent was used to precipitate pure nickel on the powder particles. The necessary nickel for obtain Nitinol composition was precipitated during 225 min plating process. The titanium primary powder as well as plated/heat treated powder was characterized by scanning electron microscopy (SEM), energy dispersive spectrometer (EDS), X-ray fluorescence (XRF), X-ray diffraction (XRD) and differential scanning calorimetric (DSC). The As and Af temperatures of Nitinol powder were measured 17.2 oC and 31°C, respectively
کلیدواژه ها:
نویسندگان
N. Barbat
M.Sc.Student, Tehran-Jonob Azad university, Tehran, Iran
K. Zangeneh-Madar
Associate professor, Department of Materials Engineering, Malek-Ashtar University of Technology, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :