Influence of pH Value on the Morphology and Magnetic Properties of BiFeO3 Nanoparticles Synthesized via Modified Chemical Co-precipitation
محل انتشار: دهمین همایش مشترک و پنجمین کنفرانس بین المللی انجمن مهندسی مواد و متالورژی و انجمن علمی ریخته گری ایران
سال انتشار: 1395
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 349
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES10_396
تاریخ نمایه سازی: 6 اردیبهشت 1396
چکیده مقاله:
Bi based perovskite systems can be applied in information storage, sensors, spintronic and microwave devices. Co-precipitation method was proposed for the synthesis of multiferroicBiFeO3 (BFO) nanoparticles. Influence of different pH value on the purity of bismuth ferrite powders was investigated. Thermogravimetric-differentioal thermal analysis (TG-DTA) technique indicated that optimal temperature for calcination is 550 0C. The phase formation,existence of transient phases (like Bi25FeO39 and Bi2Fe4O9) and the Crystallite size were studied using X-ray diffraction (XRD). The morphological features of the nanopowders werecharacterized by field emission scanning electron microscopy (FESEM). Magnetic properties of synthesized powders were measured using vibration sample magnetometer (VSM). The results showed that the BFO powders had R3c crystal structure with crystallite size line width analysis was found to be within 30-70 nm. FESEM micrographs were showed spherical shape of particlesand it is in good agreement of particle size obtained by XRD. Magnetic hysteresis loop illustrates the sample exhibited an antiferromagnetic (AFM) order at room temperature
کلیدواژه ها:
نویسندگان
h Sangian
M.Sc. Student, Metallurgy and Materials Engineering
o Mirzaee
Associate Professor, Metallurgy and Materials Engineering, Faculty of Metallurgy and Materials Engineering, Semnan University, Semnan, Iran
m tajally
Associate Professor, Metallurgy and Materials Engineering, Faculty of Metallurgy and Materials Engineering,Semnan University, Semnan, Iran
s.a.n.h Lavasani
M.Sc. Student, Metallurgy and Materials Engineering, Faculty of Metallurgy and Materials Engineering, Semnan University,Semnan, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :