Characterization of WC–Co coating deposited on Al bronze by electrospark deposition

سال انتشار: 1396
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 350

فایل این مقاله در 11 صفحه با فرمت PDF قابل دریافت می باشد

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:

شناسه ملی سند علمی:

IMES11_314

تاریخ نمایه سازی: 7 اسفند 1396

چکیده مقاله:

In this study, WC-Co based cermet coating has been produced on an Al bronze by electrospark deposition (ESD) method. Surface morphology, chemical composition, phase composition and corrosion resistance of the coatings were investigated by scanning electron microscopy (SEM) equipped with EDS analyzer, X-Ray diffraction (XRD) and potentiodynamic polarization test. Effect of different electrical parameters were also studied. Results showed that current density had the most influence on coating thickness compared to frequency. In addition, higher spark energy did not lead to higher thickness. Surface morphology and cross section images showed the presence of splash and spattering particles on the surface as well as metallurgical bond between the substrate and coating. The corrosion resistance of coating with maximum thickness is higher than the others. Moreover, results obtained for WC-Co coating prepared in this study by ESD process is close to the ones obtained in HVOF process.

نویسندگان

Hossein Aghajani

Assistant Professor, Materials Science, Assistant Professor, Materials Engineering Department, University of Tabriz

Samira Ahmadnia

M.Sc. Materials Science, corrosion and protection;