Production of Nano-crystalline Mg(Gd)2Ni-based Powder Using High Energy Ball Milling and Subsequent Heat Treatment
سال انتشار: 1396
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 324
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES11_391
تاریخ نمایه سازی: 7 اسفند 1396
چکیده مقاله:
In the present work, high-energy milling technique using a planetary ball mill and subsequent annealing have been employed for the production of nano-crystalline powders based on Mg2Ni intermetallic compound. X-ray diffraction and scanning electron microscopy were used for the characterization of the milled products. Formation of Mg2Ni-based nanocrystallites occurred after 40 and 50h of milling using the initial binary and ternary powder mixtures with stoichiometric compositions of Mg2Ni and Mg1.8Gd0.2Ni, respectively. The calculated average Mg2Ni crystallitesize was ~8 nm at the ball to powder weight ratio of 20:1 after 60 h of milling and showed decreasing with increasing the milling time. Subsequent annealing of the milled product at a low milling time of 20 h resulted in the formation of the dominant Mg2Ni intermetallic compound.
کلیدواژه ها:
نویسندگان
Muhammad Mehdinia
Master Student, Identification and Selection of Engineering Materials, School of Metallurgy and Materials Engineering, University of Tehran.
Seyed Farshid Kashani-Bozorg
Associate Professor, School of Metallurgy and Materials Engineering, University of Tehran,
Amir Zali
Master Student, Identification and Selection of Engineering Materials, School of Metallurgy and Materials Engineering, University of Tehran,
Negar Mehraein
Master Student, Identification and Selection of Engineering Materials, School of Metallurgy and Materials Engineering, University of Tehran,