Mechanical Properties and Texture Development in a Novel Dilute Extruded Mg-Zn-Gd-Y-Nd Alloy
سال انتشار: 1398
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 412
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES13_229
تاریخ نمایه سازی: 13 آبان 1398
چکیده مقاله:
Magnesium and magnesium based alloys are suitable candidates for the purpose of functioning as an industrial material in engineering applications via alloying by rare earth elements (REs). The effect of alloying elements (Zn and REs: Gd, Y and Nd) on microstructure, texture and hardness of Mg has been here investigated by means of optical microscopy (OM), hardness test and X-ray measurements. Microstructural observation exhibits that dynamic recrystallization (DRX) resulted in a bimodal microstructure due to the occurrence of fine DRX grains along the grain boundaries while static recrystallization (SRX) provide a context for a fully recrystallized microstructure which was also accompanied by the decrease of the hardness during annealing of extruded samples. More importantly, according to texture examinations, the basal texture was strengthened after extrusion while the annealing procedure after extrusion decreased the texture intensity. It is concluded that addition of alloying elements strengthens magnesium by grain refinement and solid solution strengthening effect of alloying elements. Moreover, it is observed that annealing after extrusion gives rise to a more refined grain structure and moderate hardness value together with a weaker texture
کلیدواژه ها:
نویسندگان
Zahra Abbasi
Ph.D. student, Department of Materials Science and Engineering, School of Engineering, Shiraz University, Shiraz, Iran
Ramin Ebrahimi
Professor, Department of Materials Science and Engineering, School of Engineering, Shiraz University, Shiraz, Iran