Increasment of HDF cell attachment of PCL based nanofibers using gelatin for wound dressing application
سال انتشار: 1397
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 389
نسخه کامل این مقاله ارائه نشده است و در دسترس نمی باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ITERMED01_485
تاریخ نمایه سازی: 7 مرداد 1398
چکیده مقاله:
The aim of this study was investigation the influence of gelatin on cell proliferation of PCL based nanofibers for skin tissue engineering and wound dressing applications. Electrospinning was performed using PCL and PCL/Type B gelatin. PCL solution was prepared in chloroform/dimethylformamid ratio of 2:1 (oil phase) and gelatin solutions was prepared in acetic acid (aqueous phase). The surfactant was added into the aqueous solution then oil phase was added to the aqueous phase at room temperature and stirred for 12 h to obtain a homogenous mixture. Electrospinning was carried out using 27 KV applied voltage, 1 ml/h feed rate, and 17 cm working distance. Fibroblast cell morphology, attachment and proliferation on PCL and PCL/type B gelatin nanofibers after 1, 7, 14 days were observed under Rhodamine-DAPI staining. The DAPI micrographs of HDF cells on the nanofibrous structures show highly attachment and proliferation on the PCL/Type B gelatin nanofibers surface. The PCL/ Type B gelatin electrospun nanofibrous mats have a great potential for using as a scaffold for skin tissue engineering and wound dressing
کلیدواژه ها:
نویسندگان
Mohadeseh Akbarzadeh
Iran Polymer and Petrochemical Institute, Tehran, Iran
Mohamad ezeshki_Modaress
Burn Research Center, Iran University of Medical Science, Tehran, Iran
Mojgan Zandi
Iran Polymer and Petrochemical Institute, Tehran, Iran