Effects of Casting Speed and Runner Angle on Macrosegregation of Aluminium-Copper Alloy.
محل انتشار: مجله مکانیک کاربردی محاسباتی، دوره: 49، شماره: 2
سال انتشار: 1397
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 293
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JCAM-49-2_017
تاریخ نمایه سازی: 18 تیر 1398
چکیده مقاله:
Abstract During the solidification of binary metal alloys, chemical heterogeneities at product scale over a long distance range (1cm-1m) develop and this has detrimental effect on the resulting mechanical properties of cast products. Macrosegregation is of great concern to alloy manufacturers and end users as this problem persist. In this study, the use of process parameters namely casting speed and runner angle to reduce macro-segregation in aluminum-copper-zinc binary alloy solidification is reported. The results from optical microscope, scanning electron microscope and energy dispersive spectrometry show that these parameters significantly influenced the development, size and volume of macro-segregation. The combination of parameters namely the pouring height between 96 mm/s, 100mm/s, and runner angles between 1200, 1500 produced less segregations with improved mechanical properties within standard specification. The tensile strength (110 MPa), modulus of elasticity (6800 MPa) and 2.5 % elongation obtained in this study are within standard (88- 124 MPa), 7100 MPa and (1-25 %) respectively for this class of alloy.
کلیدواژه ها:
نویسندگان
Victoria Obiekea
Department of Metallurgical and Materials Engineering, Faculty of Engineering, University of Lagos, Akoka, Yaba, Nigeria.
Israel Sekunowo
Department of Metallurgical and Materials Engineering, Faculty of Engineering, University of Lagos, Akoka, Yaba, Nigeria.
Mike Sobamowo
Department of Mechanical Engineering, University of Lagos, Nigeria
Samson Adeosun
Department of Metallurgical and Materials Engineering, Faculty of Engineering, University of Lagos, Akoka, Yaba, Nigeria.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :