Evaluation of Durability Behavior of Geopolymer Concrete Containing Nano-Silica and Nano-Clay Additives in Acidic Media
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 296
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JCEMA-3-3_004
تاریخ نمایه سازی: 31 خرداد 1399
چکیده مقاله:
The present study mainly aims at the identification and laboratory production of geopolymer concrete with the increased resistance to acid attack. For this purpose, after evaluating the reactivity of the raw materials and their applicability in the production of geopolymer cement among the available aluminosilicate materials, the metakaolin pozzolan was selected as the appropriate raw material. After the selection of the binder and activator of sodium hydroxide, the alkali activation process was performed for the mixtures of raw materials. Then, for the initial estimate of the durability performance of geopolymer cement in acidic media, the durability of concrete samples was investigated in 1M sulfuric acid for 7, 28 and 90 days. The results showed that the nano-silica and nano-clay are effective in improving the performance of geopolymer concrete, as the addition of 3% nano-silica resulted in the 0.44% increase in the strength of the geopolymer concrete. Also, the addition of 3% nano-clay led to the increase in the strength of geopolymer samples up to 0.54. In addition, the samples are more durable in acidic media, so the weight loss of nano-clay-containing geopolymer samples in 90 days is 1.2 times that of geopolymer concrete samples without this additive.
کلیدواژه ها:
نویسندگان
Behnam Mahboubi
Department of Civil Engineering, Faculty of Engineering, Kharazmi University, Tehran, Iran.
Zuhua Guo
Department of Civil Engineering, Soochow University, Jiangsu, China.
Hao Wu
Department of Civil Engineering, Soochow University, Jiangsu, China.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :