Effects of Various Chairside Surface Treatments on Zirconia-Resin Cement Bond Strength
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 256
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JDMT-8-1_003
تاریخ نمایه سازی: 18 تیر 1398
چکیده مقاله:
Introduction: Various surface treatments have been used to improve the adhesion of resin cement to zirconia restorations. The present study aimed to investigate the effects of different surface treatments on the bond strength of resin cement to zirconia (Y-TZP) in clinical practice. Methods: thirty square Y-TZP samples were classified into three groups of 10, including group SB (50 µm sandblasted Al2O3 particles), group B (diamond burs), and group C (control). One sample from each group was subjected to X-ray powder diffraction, scanning electron microscopy (SEM), and profilometer analysis. The shear bond strength (SBS) of zirconia-resin cement was measured using a universal testing machine at the crosshead speed of 1 mm/min until bonding failure. SBS values were analyzed using analysis of variance (ANOVA) and Tukey’s HSD test (α=0.05). Results: According to the results of ANOVA, SBS was significantly affected by the treatment method. Tukey’s HSD test showed significant differences between the groups (P<0.05). Groups SB (9.99±0.78 MPa) and B (9.30±0.67 MPa) had significantly higher SBS values compared to group C (6.47±1.33 MPa) (P<0.05), while they had no significant differences with each other in this regard (P> 0.05). In addition, SEM evaluations indicated morphological differences between the Y-TZP samples. According to the results of X-ray diffractometer, monoclinic phase transformation was observed in group SB only (28%). Conclusion: According to the results, grinding and sandblasting were both effective in chairside surface treatments for improving the bond strength of the resin cement to Y-TZP. However, it should be considered that sandblasting may cause phase transformation.
کلیدواژه ها:
نویسندگان
Elif Yeğin
Assistant Professor, Biruni University, Faculty of Dentistry, Department of Prosthodontics, Istanbul, Turkey
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :