Microstructural Investigation of BaTiO3 Plasma Sprayed Coating Deposited by Splash and Disk-Like Splats
محل انتشار: مجله مواد دوستدار محیط، دوره: 2، شماره: 1
سال انتشار: 1397
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 463
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JEFM-2-1_001
تاریخ نمایه سازی: 25 تیر 1398
چکیده مقاله:
In the thermal spray process, particulate materials can be melted by plasma atmosphere due to its high local temperature from 8700 ◦C to 15,000 ◦C. Therefore, the material powders turn into droplets after being melted by injection into the hot flame. Molten droplets are accelerated toward a substrate and form the splats which quickly solidify; finally, the film is formed by pile-up splats. Splat morphology and post treatment can determine the microstructure, mechanical and physical properties of the coating. In this study, BaTiO3 films were deposited onto a mirror polished stainless steel substrates kept at room temperature and 500 ◦C. At the elevated temperatures, the desorbtion of adsorbates and condensate at the substrate surface are the most important factor which change the morphology of the splats, from irregular- splash morphology to disk-like shape. Splat morphology can determine sprayed film microstructure and effect on the coating properties. The morphology of individual splats and the post treated films were studied using scanning electron microscopy. Results indicated that the porosity in the film produced at room temperature was higher than that in the film deposited on the heated substrates. Also, results show post heat treatment can improve physical and mechanical properties of the sprayed coating.
کلیدواژه ها:
نویسندگان
A.H. Pakseresht
Institute of Materials and Energy, Meshkin Dasht, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :