Synthesis and characterization of nHA-PLA composite coating on stainless steel by dip-coating process for biomedical applications
سال انتشار: 1397
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 488
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JITF-1-2_002
تاریخ نمایه سازی: 19 خرداد 1398
چکیده مقاله:
316L stainless steel is the most commonly used metallic material in the manufacture of orthopedic implants. To achive better properties metal implants often coated with biocomposites. A sol–gel method was used for coating of Poly lactic acid (PLA)/Hydroxyapatite nanopowder (nHA) on stainless steel 316L substrate. The X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) were utilized in order to evaluate the phase composition and the functional groups of PLA/nHA coatings. Morphology and thickness of the nanocomposites coating of samples were evaluated using scanning electron microscope (SEM). Cell viability asses and eventually corrosion resistance evaluated by MTT and potentiostat test, respectively. SEM result shows that the deposition rate is measured (in terms of coating thickness) as a function of immersion/soaking time. The results of XRD and FTIR tests confirmed the presence of phase of PLA/nHA nanocomposites in the coated samples. Moreover, the cellular behavior of coating was analyzed by the cell proliferation (MTT assay). Furthermore, the corrosion resistance of coated samples was increased with immersion or soaking time in the solution bath of PLA/nHA nanocomposites and was higer than the uncoated sample.
کلیدواژه ها:
نویسندگان
Monireh Ganjali
Advanced Materials and Nanotechnology Department, Materials and Energy Resaerch Center (MERC)
Shaahin Mohammadzadeh Asl
Advanced Materials and Nanotechnology Department, materials and Energy Research Center
Mahdi Alizadeh
۲Department of Materials Engineering, Isfahan University of Technology, Iran, Isfahan
Mona Shahlaei
Nanotechnology and Advanced materials, Materials and Energy Research Center (MERC), Iran, Tehran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :