Investigation of Dip-Coating Parameters Effect on The Performance of Alumina-Polydimethylsiloxane Nanofiltration Membranes for Desalination

The objective of this work is to investigate the effect of dip-coating parameters on the performance of Alumina-PDMS hybrid nanofiltration membranes for water desalination. Ceramic supports used in this work were prepared with a 340 nm average pore size and 34% total porosity. The aim is to determine optimum conditions of dipping time, PDMS concentration, and withdrawal speed in order to achieve high rejection and flux values. Dip-coating parameters were considered as dipping time (60 - 120 s), withdrawal speed (5 - 15 mm/s) and PDMS concentration (10 - 20 wt. %). Hybrid membranes were characterized using FE-SEM and FTIR analysis techniques. Pure water flux and salt rejection were also measured to evaluate the rejection performance. Alumina-PDMS hybrid nanofiltration membranes fabricated with dipping time = 120 s, withdrawal speed = 15 mm/s and 10 wt. % PDMS exhibited the best performance giving 30.5% rejection for NaCl and 53.8% for Na2SO4.

کلیدواژه ها:

Alumina ، Dip-Coating ، Hybrid Membranes ، Nanofiltration ، PDMS