Effects of ultrasound on properties of ni-metal organic framework nanostructures
محل انتشار: مجله علوم نانو، دوره: 3، شماره: 4
سال انتشار: 1395
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 348
فایل این مقاله در 5 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_NAMJ-3-4_006
تاریخ نمایه سازی: 18 تیر 1398
چکیده مقاله:
Objective(s): According to the unique properties of magnetic nanoparticles, Nickel Metal-Organic Frameworks (MOF) was synthesized successfully by ultrasound irradiation. Metal-organic frameworks (MOFs) are organic–inorganic hybrid extended networks that are constructed via covalent linkages between metal ions/metal clusters and organic ligands called a linker. Materials and Methods: The nanoparticles were synthesized by Ultrasound Method Under a synthesis conditions, All chemicals were used as received without further purification. Scanning electron microscopy (SEM) images were obtained on LEO- 1455VP equipped with an energy dispersive X-ray spectroscopy at university of Kashan in Iran. Transition electron microscopy (TEM) images were obtained on EM208 Philips transmission electron microscope with an accelerating voltage of 200 kV. Results: Results showed that Ni-MOF synthesized by this method, had smaller particle size distribution and It was found that the different kinds of ligand leads to preparation products with different morphologies and textural properties. Moreover, ultrasound irradiation method has significant effect on microstructures of as-synthesized MOFs and can improve their textural properties compared to method without using hydrothermal route.The XRD patterns of the samples obtained from ultrasound irradiation was well matched with that of as-prepared Ni-MOF by solvothermal method. Conclusion: This rapid method of ultrasonic radiation as compared to the classical solvothermal synthesis, showed promising results in terms of size distribution, surface area, pore diameter and pore volume.
کلیدواژه ها:
نویسندگان
Abbas Pardakhty
Pharmaceutics Research Center, Institute of Neuropharmacology, Kerman University of Medical Sciences, Kerman, Iran
Mehdi Ranjbar
Department of Chemistry, Kerman Branch, Islamic Azad University, Kerman, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :