Preparation, characterization and antimicrobial property of ag+- nano Chitosan/ZSM-5: novel Hybrid Biocomposites
محل انتشار: مجله علوم نانو، دوره: 3، شماره: 4
سال انتشار: 1395
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 325
فایل این مقاله در 12 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_NAMJ-3-4_008
تاریخ نمایه سازی: 18 تیر 1398
چکیده مقاله:
Objective(s): Binary hybrids of chitosan-zeolite have many interesting applications in separation and bacteriostatic activity. Materials and Methods: Template free ZSM-5 zeolite was synthesized by hydrothermal method, physical hydrogels of nano chitosan in the colloidal domain were obtained in the absence of toxic organic solvent and then nano chitosan/ZSM-5 hybrid composites with nano chitosan contents of 0.35%, 3.5%, 35% wt.% were prepared. The as prepared hybrid composites were ion-exchanged with Ag cations. Results: XRD and FT-IR results revealed a good crystalinity of as synthesized template frees ZSM-5 with BET surface area of 307 m2g-1. Presence of chitosan in composites was confirmed by XRD patterns and FT-IR spectroscopic analysis, the chitosan content in composite was obtained with TG analysis. SEM analysis of composites shows that chitosan particles were dispersed within the nanometer scale. The antimicrobial activity of different samples was investigated and the results showed that the Ag+-exchanged samples have the highest antibacterial properties. Cancer cell line A549 cell line were cultured in designated medium treated with Ag+-exchanged samples at the concentration of 0.01 to 0.5 mg/ml. After 24 and 48 hours incubation, the efficacy of Ag+-exchanged samples to treat cancer cell lines were measured by means of cell viability test via MTT assay. Concentrations of 0.05 and 0.1 mg/ml of Ag+-exchanged samples induced a very low toxicity. Conclusion: These hybrid composite materials have potential applications on tissue engineering and antimicrobial food packaging.
کلیدواژه ها:
نویسندگان
Maasoumeh Khatamiana
norganic Chemistry Department, Faculty of Chemistry, University of Tabriz, Tabriz, Iran
Baharak Divband
norganic Chemistry Department, Faculty of Chemistry, University of Tabriz, Tabriz, Iran|Research Center for Pharmaceutical Nanotechnology, Tabriz University of Medical Sciences, Tabriz, Iran
Mahdieh Daryana
norganic Chemistry Department, Faculty of Chemistry, University of Tabriz, Tabriz, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :