Mathematically and experimentally defined porous bone scaffold produced for bone substitute application
محل انتشار: مجله علوم نانو، دوره: 5، شماره: 4
سال انتشار: 1397
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 403
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_NAMJ-5-4_007
تاریخ نمایه سازی: 18 تیر 1398
چکیده مقاله:
Objective (s): Artificial bone implants have been studied as a possible bone replacement for fractured and destroyed facial tissue; the techniques employed to determine the success of the dental implants. The stability, porosity and resistance of the bone implant which is subjected to varying forces and stresses within the surrounding bone is a subject of interest among the dentists. Materials and Methods: An experimental analysis was conducted on bio-nanocomposite scaffold using space holder methods. The reaction of the bio-nanocomposites deformation under load was determined using Abaqus software. Thereafter, an analytical solution was presented to express explicitly the deformation responses of the artificial bone implant. Results: It was seen that the vibrational behavior and mechanical performance of the sample containing 15 wt% additives have shown better mechanical characteristic compared to the pure specimen. On the other hand, the additive weight fraction has a significant effect on the compression test and porosity value. Also, the elastic modulus of the samples increases more than two times with the addition of additive (from 60 MPa to 145 MPa). From the results, it can be concluded that the highest vibration variation is seen in the sample with lower MNPs percentages.Conclusion: By observing the results of the stresses, it was seen that the stresses were in a small value in the bio-nanocomposites with highest amount of reinforcement.
کلیدواژه ها:
نویسندگان
Hamed Joneidi Yekta
New Technologies Research Center, Amirkabir University of Technology, Tehran ۱۵۸۷۵-۴۴۱۳, Iran
Maryam Shahali
Department of Quality Control, Research and Production Complex, Pasteur Institute of Iran, Tehran, Iran
Siros Khorshidi
New Technologies Research Center, Amirkabir University of Technology, Tehran ۱۵۸۷۵-۴۴۱۳, Iran
Soheila Rezaei
Department of Molecular Genetic, National Institute of Genetic Engineering and Biotechnology, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :