Thermal behavior of ethylene/1-octene copolymer fractions at high temperatures: Effect of hexyl branch content
محل انتشار: فصلنامه پلی اولفین ها، دوره: 6، شماره: 2
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 465
فایل این مقاله در 12 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_POJ-6-2_003
تاریخ نمایه سازی: 5 مرداد 1398
چکیده مقاله:
In this work, the effect of hexyl branch content on thermal behavior of a fractionated ethylene/1-octene copolymer with emphasis on high temperatures was investigated. The ethylene/1-octene copolymer was carefully fractionated to different fractions with homogenous hexyl branch (HB) content by preparative temperature rising elution fractionation (P-TREF) method. The P-TREF fractions were thermally analyzed via differential scanning calorimetry (DSC), thermogravimetric analysis (TGA) and evolved gas analysis (EGA). The P-TREF profile showed a short chain branch distribution (SCBD) of around 1.24. A linear relationship between P-TREF elution temperature (ET) and methylene sequence length (MSL) was presented. The DSC curves exhibited a monolithically increase in melting temperature (Tm) as well as crystallization temperature (Tc) by decreasing short chain branch (SCB) content. The calculated values of lamellae thickness suggested a linear function of SCB content and Tm. The TGA studies of P-TREF fractions depicted a two-stage thermal degradation behavior: pre-degradation and main degradation stages. Tmax for both pre-degradation and main degradation stages was increased for fractions with less hexyl branch content. As an interesting point the pre-degradation stage was found more intensified for more linear fractions. The concentration of main products was found to be affected by the content of hexyl branches using Py-GC-MS.
کلیدواژه ها:
نویسندگان
Abbas Kebritchi
Iran Polymer and Petrochemical Institute, ۱۴۹۶۵-۱۱۵, Tehran, Iran
Mehdi Nekoomanesh
Iran Polymer and Petrochemical Institute, ۱۴۹۶۵-۱۱۵, Tehran, Iran
Fereidoun Mohammadi
Iran Polymer and Petrochemical Institute, ۱۴۹۶۵-۱۱۵, Tehran, Iran
Hossein Khonakdar
Iran Polymer and Petrochemical Institute, ۱۴۹۶۵-۱۱۵, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :