Insights into the effect of vanadium on chromium-vanadium Phillips catalysts for the ethylene polymerization
محل انتشار: فصلنامه پلی اولفین ها، دوره: 7، شماره: 2
سال انتشار: 1399
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 255
فایل این مقاله در 18 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_POJ-7-2_001
تاریخ نمایه سازی: 15 مرداد 1399
چکیده مقاله:
The chromium/vanadium bimetallic Phillips catalysts developed by our research group have been proved to be a promising process to produce bimodal polyethylene using a single-reactor process. The vanadium loading of CrV-1/1, CrV-1/2, and CrV-1/3 has a significant effect on the polymerization activity, product molecular weight (MW), as well as the molecular weight distribution (MWD). Due to the unstable and easy deactivation of vanadium active centers at atmospheric or low (0.4 MPa) reaction pressure [Macromol. React. Eng. 2015, 9, 462–472], the reaction is carried out at 1.0 MPa to strength the V active center on the activities of ethylene homopolymerization, ethylene/1-hexene copolymerization, and the H2 responds properties. The reaction carried out at higher pressure promotes the polymerization activities. With the same amount of cocatalyst, the highest activity of the three Cr-V bimetallic catalysts CrV-1/1, CrV-1/2 and CrV-1/3 decreases with the increase of vanadium loading. The Cr-V bimetallic catalysts require more cocatalyst than the single metal Cr cat. It was found two obvious peaks in the GPC curves of homopolyethylen and ethylene/1-hexene copolymer. It means that the higher reaction pressure benefits the promotion of the active center of catalyst for higher MW. By increasing the loading from 0.48 wt.% (CrV-1/1) to 0.96 wt.% (CrV-1/2), the molecular weight increases by nearly 30%. Besides, according to the deconvolutions of the GPC curves of homopolymers, ethylene/1-hexene copolymers, and the homopolymers with H2 modulation, the synergetic effect between Cr and V center is presented. As the vanadium loading increases, the active site accounted for the high molecular weight portion increases, and the Cr-V catalyst presents better hydrogen responds. When the partial pressure of hydrogen is 0.1 MPa, the molecular weight is reduced by nearly half. Specifically, the high molecular weight peak is weakened, while the low molecular weight peak is strengthened. The peak position does not change significantly. The higher vanadium content and the greater sensitivity of hydrogen modulation indicate that the vanadium active center has better hydrogen responds than the chromium active center does. The homopolymerization product of the Cr/V-1/1 catalysts exhibits higher tensile strength and elongation-at-break. The tensile properties of the copolymerized product of CrV-1/1 are further improved.
کلیدواژه ها:
نویسندگان
Shijia Ling
State Key Laboratory of Chemical Engineering, East China University of Science and Technology, Meilong Road ۱۳۰, Shanghai ۲۰۰۲۳۷, China
He Ren
Daqing Petrochemical Research Center, CNPC, NO.۲ Chengxiang Road, Daqing, Heilongjiang ۱۶۳۰۰۰, China
Rui Zhang
Daqing Petrochemical Research Center, CNPC, NO.۲ Chengxiang Road, Daqing, Heilongjiang ۱۶۳۰۰۰, China
Yue Liu
State Key Laboratory of Chemical Engineering, East China University of Science and Technology, Meilong Road ۱۳۰, Shanghai ۲۰۰۲۳۷, China
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :