Synthesis and characterization of gelatin based scaffold with 1 sufficient mechanical properties for bone implant
سال انتشار: 1395
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 822
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
MECHCONF01_246
تاریخ نمایه سازی: 21 شهریور 1395
چکیده مقاله:
In the current study freeze casting method was employed to fabricate highly porous gelatin/ akermanite scaffolds. 10 Gelatin(GEL) based nanocomposite scaffolds were prepared a controlled unidirectional freeze casting through blending constant gelatin concentration with Akermanite nanoparticles (AKRNPs). Pore morphology, mechanical properties, and water adsorption characteristics of scaffolds were assessed. The compressive strength and elastic module values was 5.46 MPa, and 2.86 GPa, respectively. Scanning Electron Microscopy (SEM) images depicted a unidirectional structure with homogenous distribution of AKR among gelatin matrix.
کلیدواژه ها:
نویسندگان
Azam Zare Harofte
Material and Biomaterial Research Center, Tehran, Iran
Samaneh Saber-Samandari
Department of Chemistry, Eastern Mediterranean University, Gazimagusa, TRNC via Mersin 10, Turkey
Saeed Saber-Samandari
Material and Biomaterial Research Center, Tehran, Iran New Technologies Research Center, Amirkabir University of Technology, Tehran, Iran
Ali Zamanian
Materials and Energy Research Center, Alborz, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :