Formation Mechanism of TiCr2 Intemetallic by Calciothermic co-reduction Method
محل انتشار: اولین کنفرانس بین المللی مواد پیشرفته
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 2,160
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
NAMIC01_074
تاریخ نمایه سازی: 18 تیر 1391
چکیده مقاله:
In this work, TiCr2 intermetallic was successfully synthesized by calciothermic co-reduction of the TiO2 and Cr2O3 powders. Differential thermal analysis and X-ray diffraction were used for determining the formation mechanism of this compound. It was found that the molten Ca reacts with Cr2O3 through an exothermic reaction at about 933°C and Cr and CaO were formed. By increasing the temperature, CaTiO3 was formed because of the reaction of CaO and TiO2. As the temperature increased to about 1063°C, Ti was formed because of the Ca reaction with the remained TiO2 and CaTiO3 through an exothermic reaction. Finally, TiCr2 was formed by the mutual diffusion of Ti and Cr elements. The obtained TiCr2 powder contained 1690 ppm oxygen and showed the capability of a hydrogen absorption material after activation
کلیدواژه ها:
نویسندگان
O. Bayat
School of Metallurgy and Materials Engineering, Iran University of Science and Technology (IUST), Tehran ۱۶۸۴۶-۱۳۱۱۴, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :