Synthesis and Characterization of zinc powder using reduction method by natural gas
محل انتشار: اولین کنفرانس بین المللی مواد پیشرفته
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,348
فایل این مقاله در 5 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
NAMIC01_087
تاریخ نمایه سازی: 18 تیر 1391
چکیده مقاله:
Zinc nano powder was produced by a novel efficient process. The procedure of synthesis is the combination of reforming of natural gas and reducing of zinc oxide in a single unit. This phenomenon involves the reduction of zinc oxide by natural gas as a reducing agent for production of zinc vapors. Then the condensation of solid particles occurs on a low temperature copper substrate which is placed at the end of the furnace tube. Zn particles with an average crystallite size of 57.9nm were formed. Since most properties of fine particles are size dependent, the particle size as a critical property have been determined in this article. Different characterization methods such as X-ray diffractometry (XRD), scanning electron microscopy (SEM), laser particle size analyzer and energy-dispersive X-ray spectroscopy (EDX) were used. Effect of parameters on average particle size of samples was investigated
کلیدواژه ها:
نویسندگان
S Rahimi
Materials engineering department, Sahand University of Technology, Tabriz, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :